Ceramic fiber paper is a precision-engineered, flexible high-temperature insulation sheet manufactured from high-purity spun aluminosilicate ceramic fibers via an automated wet-laid fourdrinier papermaking process. Providing continuous thermal resistance from 1260°C to 1430°C with an engineered bulk density of 180 to 220 kg/m³ and standard thicknesses spanning 0.5 mm to 10 mm, ceramic fiber paper delivers tensile strength exceeding 0.40 MPa, shot content below 8.0%, and excellent dielectric breakdown resistance (>1.2 kV/mm).
Atravè entènasyonal laseramik fib papye mache, materyèl sa a versatile te lajman ranplase dra lenn mouton mineral, papye amyant, ak fèy mika wo-tanperati nan aplikasyon ki mande mens-seksyon kwa baryè tèmik. Soti nan garnitur bride founo mouri-koupe ak vlope ekspansyon gòj brûler rive nan baryè ki pa FERROUS metal fonn separe, papye fib seramik bay yon sele tèmik ki lejè. Anba a se klas klasifikasyon kle yo, mezi rekiperasyon konpresyon, pèfòmans dyelèktrik, ak espesifikasyon akizisyon faktori.
Ki sa ki papye fib seramik refractory (RCF)? (Pwosesis la mouye)
Kontrèman ak dra fib seramik zegwi-perfore, ki konte sou fib mekanik entè-tangling, papye fib seramik fòme atravè yon pwosesis espesyalize endistriyèl fè papye ki garanti epesè inifòm, fini sifas lis, ak pwopriyete izotwòp mekanik:
Sispansyon ak lave fib:Fibre aluminosilicate esansyèl (Al₂O₃ 45-50%, SiO₂ 50-55%) yo gaye nan dlo. Patikil vè esferik lou, san fib (ki rele "piki") yo separe ak jete sikonikman, sa ki diminye kontni piki a.<8% (and <5% in premium grades).
Mesure Binder:Yon lyan an latèks òganik propriétaires (6.0-8.5% nan pwa) yo mezire nan sispansyon an fib akeuz. Lyan sa a kouvri fib endividyèl yo, bay fòs vèt limenm, fleksibilite elongasyon, ak woule.
Drenaj Fil Fourdrinier:Sispansyon an ap koule kontinyèlman sou yon ekran fil fourdrinier k ap deplase kote bwat vakyòm rapidman dezidrate mat fib la, oryante fib nan yon plan inifòm miltidireksyon.
Kalandriye ak geri lè cho:Fèy mouye a pase nan woulèt konpaksyon chofe (kalandriye) ki konsolide epesè nan tolerans egzak (± 0.1 mm) anvan yo antre nan yon tinèl konveksyon milti-zòn pou geri polymère òganik la.
Precision Slitting & Liquidation:Woulo fini kontinyèl la koupe kwen ak blese sou nwayo katon lou nan lajè estanda 610 mm, 1000 mm, oswa 1220 mm.
Espesifikasyon teknik: Standard, High-Purity & Zirconia Klas
Chwazi klas apwopriye a nan mache papye seramik mondyal la mande pou matche tanperati opere, atmosfè chimik, ak kondisyon mekanik:
1. Estanda 1260 degre Klas (Jeneral Endistriyèl izolasyon)
Tanperati klasifikasyon:1260 degre (sèvis kontinyèl: mwens pase oswa egal a 1050 degre)
Analiz Chimik:Al₂O₃ 45–47%, SiO₂ 51–53%, Fe₂O₃ mwens pase oswa egal a 0.8%
Dansite esansyèl:180-210 kg / m³
Fòs rupture:Longitudinal Pi gran pase oswa egal a 0.40 MPa; Transverse Pi gran pase oswa egal a 0.30 MPa (ASTM D828)
Shot Content (>45 μm):Mwens pase oswa egal a 8.5% (ASTM C612)
Pèt sou ignisyon (LOI):Mwens pase oswa egal a 8.0%
Kondiktivite tèmik:0.075 W/m·K nan 400 degre; 0.145 W/m·K nan 800 degre; 0.210 W/m·K nan 1100 degre
2. High-Purity 1350 degre Klas (Pwòp Tire & Low Enpurte)
Tanperati klasifikasyon:1350 degre (sèvis kontinyèl: mwens pase oswa egal a 1150 degre)
Analiz Chimik:Al₂O₃ 47–49%, SiO₂ 50–52%, Alkali total (Na₂O + K₂O) Mwens pase oswa egal a 0.2%
Dansite esansyèl:190-220 kg/m³
Fòs rupture:Longitudinal Pi gran pase oswa egal a 0.45 MPa; Transverse Pi gran pase oswa egal a 0.35 MPa
Shot Content (>45 μm):Mwens pase oswa egal a 6.0%
Pèt sou ignisyon (LOI):Mwens pase oswa egal a 7.0%
Kondiktivite tèmik:0.070 W/m·K nan 400 degre; 0.138 W/m·K nan 800 degre; 0.195 W/m·K nan 1100 degre
3. Zirconia 1430 degre klas (sèvis tèmik grav)
Tanperati klasifikasyon:1430 degre (sèvis kontinyèl: mwens pase oswa egal a 1300 degre)
Analiz Chimik:Al₂O₃ 35-39%, SiO₂ 44-48%, ZrO₂ 15-18%
Dansite esansyèl:200-230 kg / m³
Fòs rupture:Longitudinal Pi gran pase oswa egal a 0.50 MPa; Transverse Pi gran pase oswa egal a 0.40 MPa
Shot Content (>45 μm):Mwens pase oswa egal a 5.0%
Pèt sou ignisyon (LOI):Mwens pase oswa egal a 6.5%
Kondiktivite tèmik:0.068 W/m·K nan 400 degre; 0.132 W/m·K nan 800 degre; 0.180 W/m·K nan 1100 degre
Avantaj zirkonya:Anplis de sa nan 15-18% ZrO₂ inibit mullite kristal grosye ak vitreous silica devitrification pi wo a 1150 degre, byen wo diminye apre tire kontraksyon.
Tèmik ekspansyon Joint konsepsyon: Konpresibilite & Recovery
Lè w ap desine garnitur bride wo-tanperati oswa bag sele brûler, konpresibilite mekanik ak rekiperasyon dikte si yon jwenti rete san koule:
Mekanik konpresibilite:Anba yon premye estrès syèj boulon nan 0.1 MPa, estanda 3 mm papye fib seramik konpresyon pa 25% a 32%, diminye epesè a apeprè 2.1 mm. Konpresyon elastik sa a fòse fib aluminosilikat mou nan iregilarite sifas, mak zouti, ak twou vid ki genyen deformation sou asye ki pa machin oswa kas-fè bride. Anba chaj boulon 0.5 MPa, konpresyon rive nan 45% a 55%.
Rezilyans rekiperasyon elastik:Kontrèman ak fèy grafit oswa elastomerik, papye fib seramik montre yon pousantaj rekiperasyon mekanik 18% a 25% lè yo lage chaj. Nan founo pakèt siklik kote boîtri elaji ak kontra dinamik, rezistans fib rezidyèl sa a anpeche kreyasyon mikwo-gaps ki pèmèt gaz ki ka pran dife oswa kontourne lafimen.
High-Tanperati elektrik ak izolasyon Dielectric
Yon kapasite papye fib seramik souvan neglije se fòs pann elektrik li nan tanperati ki wo:
Fòs pann dyelèktrik: Measured per ASTM D149, dry ceramic fiber paper delivers an electrical breakdown strength of >1.2 to 1.5 kV/mm at room temperature, maintaining >0.8 kV / mm menm apre chofaj sot pase 800 degre.
Rezistans sifas:Plis pase 10¹² Ω·cm nan kondisyon sèk, anpeche arcing elektrik ant eleman chofaj wo-vòltaj ak kokiy founo ki chita. Itilize lajman kòm séparateur faz ak vlope busbar nan inite k ap fonn endiksyon ak liy trase chalè endistriyèl.
Aplikasyon Endistriyèl & Kowòdinasyon Milti-Materyèl
1. Petrochemical & Industrial Kiln Flange Joints
Nan rafineri aparèy chofaj fann ak fou tinèl seramik aliyen akbrik refractory tanperati ki wo, linèt je, blòk brûler, ak bride klape tiyo echapman mande pou ranplasman rapid gasket pandan are.
Benefis:Konpòtman ki pa baton kont anvlòp metal; fasil grate pwòp pandan vire chak ane san yo pa domaje fas sele bride.
2. Transfè aliminyòm fonn & blanchi
Nan fusion aliminyòm ak depoze, metal fonn (700 degre a 850 degre) pa pral mouye oswa reyaji ak fib aluminosilicate. Papye fib seramik sèvi kòm yon revètman lage sakrifis andedan blanchi, vide becs, ak jete bouch, pwoteje kache.gwo dansite kalsyòm silikat tablo.
3. Glass Recuit Lehrs & Precision Ceramic Tire
Kontak dirèk ak brik refractory difisil ka grate gwo valè fèy vè achitekti oswa lakòz kwen-chipping sou substrats seramik teknik. Fèy papye fib seramik 1 mm oswa 2 mm ki mete sou foyer machin fou yo bay yon kousen tèmik san friksyon, ki pa grate pandan refwadisman.
Pou revètman gwo founo ki mande dra izolasyon kontinyèl olye ke fèy papye mens, kontraktè marye papye sa yo akdra seramik fib pou pawa gwo founo difepou reyalize konplè tèmik patiraj.
Konvèti presizyon: koupe, fè bak PSA ak koupe mouri
tprefractory bay anpil kapasite konvèti koutim dirèkteman nan plant manifakti nou an:
Koutim woulo liv lajè koupe:Gwo vitès nòt-tache desann nan lajè koutim osi etwat ke 20 mm pou aplikasyon pou espiral tiyo-vlope.
Fè bak adezif ki sansib a presyon (PSA):Pou enstalasyon vètikal (egzanp, kole garnitur nan ankadreman pòt founo vètikal anvan boulon), nou aplike yon fim transfè adezif ki gen gwo tach kale ak baton sou yon bò. Adezif la boule nèt lè inisyal chofaj pi wo a 250 degre.
Fabrikasyon Joint mouri-koupe:Près mouri konplètman otomatize fabrike garnitur brûler konplèks, bag manway oval, ak woulo kasèt kontinyèl ak modèl twou boulon nan espesifikasyon CAD kliyan yo.
Dimansyon ekspòtasyon, anbalaj & Gid sourcing faktori
Kòm yon manifakti verifye nan Lachin, tprefractory bato tout woulo ekspòtasyon nan anbalaj imidite ki pwoteje ki te bati pou anbake veso milti-semèn.
Konfigirasyon woulo liv estanda
0.5 mm epesè:Lajè 610 / 1000 / 1220 mm|Longè woulo liv: 60 m (36.6 a 73.2 m²)
1.0 mm epesè:Lajè 610 / 1000 / 1220 mm|Longè woulo liv: 40 m (24.4 a 48.8 m²)
2.0 mm epesè:Lajè 610 / 1000 / 1220 mm|Longè woulo liv: 20 m (12.2 a 24.4 m²)
3.0 mm epesè:Lajè 610 / 1000 / 1220 mm|Longè woulo liv: 15 m (9.15 a 18.3 m²)
5.0 mm epesè:Lajè 610 / 1000 / 1220 mm|Longè woulo liv: 10 m (6.10 a 12.2 m²)
6.0 mm epesè:Lajè 610 / 1000 / 1220 mm|Longè woulo liv: 8 m (4.88 a 9.76 m²)
10.0 mm epesè:Lajè 610 / 1000 mm|Longè woulo liv: 5 m (3.05 a 5.0 m²)
Regleman Komèsyal & Asirans Kalite
Kantite Lòd Minimòm (MOQ):20 woulo stock estanda; 1,000 moso pou koutim mouri-koupe garnitur.
Tan plon faktori:Epesè stock estanda voye nan 5-7 jou travay; koutim mouri-koupe garnitur pran 10-14 jou travay.
Verifikasyon Kalite:Chak anpil ekspòtasyon teste pou dansite esansyèl, pèt sou ignisyon (LOI), ak fòs rupture. Sètifika Tès Mill konplè (MTC) akonpaye manifeste anbake yo.
Lojistik:FOB Kendao Port oswa CIF livrezon atravè lemond. Yo sipòte chajman veso konsolide ak brik dife, castables, ak dra fib seramik pou optimize pri machandiz yo.
Sipò teknik ak demann RFQ
Pou mande fèy done teknik (TDS), rapò tès materyèl, oswa yon sitasyon pou woulo mèt ak garnitur koutim:
Imèl: inquiry@topower.tech (Repons dirèk enjenyè nan lespas 4 èdtan)
Detay ki nesesè pou Joint Quotes:Tanperati opere, presyon boulon bride, ak desen 2D (PDF/DWG) ak dimansyon ak tolerans.